Crusher Liner

Crusher liners, the mainly replacement parts for crusher, the mainly wear parts for crusher,which also called crusher casting parts. JYS foundry liner are independently proven in mining and aggregate production to achieve, and often exceed the performance of the original OEM foundries products. JYS foundry that has been developed from the original Hadfield’s manganese steel specification, we can provide unequalled toughness with excellent resistance to abrasion, which improves as the steel work hardens in operation.

Crusher Liner In Different Crusher Types

There are so many kinds of stone crusher. Jaw crusher, cone crusher,impact crusher,VSI Sandmaking Crusher and other.In different crusher, it has different crusher liner.

Jaw Crusher Impact Crusher Cone Crusher VSI Crusher Primary Gyratory 
Fixed jaw plate
Movable jaw plate
Protect plate
Side Plate
Blow bars
Impact plate
Side plate
Cone liner
Bowl liner
Torch ring
Carbide Tips
Feed Tube
Feed Eye Ring
Upper & Lower Wear Plates
VSI Rotor
VSI Center Cone
Cone Liner
Bowl Liner
Wear Plate

Crusher Liner Material

  • Austenitic manganese steel. Austenitic manganese steel is a very tough and ductile material having a high impact toughness. Mn-steel is rather soft material having an initial hardness of approx. 220-250 HV. The wear resistance of manganese steel is based on a work hardening phenomenon.The original austenitic manganese steel, containing about 1.2% C and 12% Mn, was invented by Sir Robert Hadfield in 1882. Hadfield`s steel was unique in that it combined high toughness and ductility with high work-hardening capacity and, usually, good resistance to wear.
Element C Si Mn Cr S P Mo Cu Ni Re
 Per(%) 0.90-1.30 ≦0.08 11.00-23.00 1.50-2.50 ≦0.04 ≦0.06 ≦0.5 ≦0.004 ≦1.0 /
Mechanical Property
Equivalent Material Standard :GB/T5680-1998 DL/T681-199 JIS G5153-1999 ASTM A 128
DINGX120Mn12 AFNORZ120Mn11Material Application: Jaw plate,Concave and Mantle,Side Plate, Wear Plate
  • High chromium steel. These materials are of low cost, and good choise for many applications. The wear resistance is based on the hard carbides on the relative hard matrix, still the composition and structure can be tailored considerably. Generally high cromium irons are commonly used in abrasive wear applications.
Element Per(%) C Si Mn Cr S P Mo Cu Ni Re
High Cr Alloy Steel 1.1-2.2 0.6-1.2 0.5-1.0 11.0-33.0 ≦0.04 ≦0.06 0.1-3.0 0.1-1.0 0.1-1.0 0-0.3
High Cr White Steel 2.4-3.2 0.6-1.2 0.5-1.0 11.0-33.0 ≦0.04 ≦0.06 0.1-3.0 0.1-1.0 0.1-1.0 0-0.3
Equivalent Material Standard :GB/T5680-1998 DL/T681-199 JIS G5153-1999 ASTM A 128
AS2027 Cr27Material Application: high chrome blow bars,crusher hammer

Crusher Liner For Brands

Pegson, Cedarapids, , Extec,Finlay, Finte  Hart’l, Hazemag, Hewitt Robins, , Kleeman Reiner, Kobelco, Komatsu, Krupp, Kue Ken, Lokomo, Metso Minerals™, Minyu, Morgardshammar, Neyrtec, Nordberg, Officine Mechaniche, OM, Osborn, Parker, Pegson, Pegson-Telsmitht, Powerscreen-Pegson, Sandvik™, SBM, , Svedala, Symons, Telsmith, Terex-Finlay, Terex-Pegson, Tesab ,Shanbao, Shanmei,Huayang, Shuangjing,Liming,Xuanshi…..